Grade | Ni | Cu | Fe | Mn | C | Si | S |
UNS N02200 | ≥99.00 | ≤0.25 | ≤0.40 | ≤0.35 | ≤0.015 | ≤0.35 | ≤0.01 |
UNS N02201 | ≥99.00 | ≤0.25 | ≤0.40 | ≤0.35 | ≤0.02 | ≤0.35 | ≤0.01 |
Sign In | Join Free | My frbiz.com |
|
Brand Name : Shangle
Model Number : 12.7
Certification : PED,IS09001
Place of Origin : CHINA
MOQ : Negotiable
Price : Negotiable
Payment Terms : L/C, T/T
Supply Ability : 500TONS/30DAYS
Delivery Time : 30DAYS
Packaging Details : Woven Packing
Material : Nickel Alloy
Standard : AISI, ASTM, DIN, EN, GB
Shape : SCH10, SCH20, SCH30, STD, SCH40, SCH60, SCH80
Technique : Cold Draw
Application : Oil, Petroleum/Power
Package : Woven Packing
Grade | Ni | Cu | Fe | Mn | C | Si | S |
UNS N02200 | ≥99.00 | ≤0.25 | ≤0.40 | ≤0.35 | ≤0.015 | ≤0.35 | ≤0.01 |
UNS N02201 | ≥99.00 | ≤0.25 | ≤0.40 | ≤0.35 | ≤0.02 | ≤0.35 | ≤0.01 |
Grade | Condition | Tensile Strength | Yield Strength | Elongation(%) |
N02201 | Annealed | ≥50(345)ksi(MPa) | ≥12(83)ksi(MPa) | ≥40 |
N02201 | Stress-relieved | ≥60(414)ksi(MPa) | ≥30(207)ksi(MPa) | ≥15 |
N02201 OD≤127MM | Annealed | ≥50000(380)psi(MPa) | ≥12000(80)psi(MPa) | ≥35 |
N02201 OD>127MM | Annealed | ≥50000(345)psi(MPa) | ≥10000(70)psi(MPa) | ≥40 |
N02201 | Stress-relieved | ≥60000(415)psi(MPa) | ≥30000(205)psi(MPa) | ≥15 |
Used primarily for parts requiring excellent corrosion and strong magnetic properties such as:
Marked Pipe Sample: XTD ASTM B163 UNS N02201 SEAMLESS 42.2x 3.56*6000MM HEAT NO. 2023121205A15
Nickel 201 alloy is a commercially pure wrought alloy having properties similar to that of nickel 200 alloy, but with a lower carbon content to avoid embrittlement by inter-granular carbon at high temperatures.
It is resistant to acids and alkalis, and dry gases at room temperature.
Alloy 201 is a wrought commercially pure Nickel with a maximum carbon level of 0.02%. This alloy provides highly ductile mechanical properties across a wide temperature range.It provides corrosion resistance in neutral to moderately reducing environments. Nickel 201 is ferromagnetic. It provides high thermal and electrical conductivity in comparison to nickel-base alloys, stainless and low alloy steels. Because of its low carbon content (.02% max.) Nickel 201 may be considered for service above 600 °F (316 °C), where alloy 200 with higher carbon content is not recommended.
![]() |
ASTM B161 B163 Nickel 201 Alloy UNS N02201/2.4068 Seamless Nickel Alloy Steel Pipe Images |